Epoxy Permabond
ET510
Description
A two-part, semi-flexible epoxy adhesive with good resistance to water, gasoline and most of oils.
Operating temperatures
-40°C +80°C
Pre-packing
200ml400ml10kg40kg400kg
- Applications
- Advantages
- Features
Applications
It is suitable for bonding a wide range of surfaces such as wood, metal, ceramics as well as many kinds of plastic and composite materials.
Advantages
- Maximum gap fill is 1.5 – 2 mm
- Setting time is > 5 min
- High flexibility (operation under vibration and temperature drop conditions)
- Resistance to acids, alkolis and solvents
- Operable under steam conditions
- Operable in wet environment
- Resistace to technical natural gases
| Стандарт | Показатель | Ед. изм. | Значение |
|---|---|---|---|
| — | Цвет | Компонент А - бесцветный; Компонент В - янтарный | |
| — | Химический тип | Двухкомпонентная эпоксидная смола | |
| — | Диапазон рабочих температур | °С | от -40 до +80 |
| — | Динамическая вязкость | Па*с | Компонент А 23; Компонент В 35 |
| — | Плотность при 25 °С | г/см3 | Компонент А 1,2; Компонент В 1 |
| — | Относительное удлинение при разрыве | % | 30 |
| — | Твердость по Шору D | 80 | |
| ISO 4578 | Прочность на отрыв | Н/25 мм | 80 |
| ASTM D 1002 | Прочность на сдвиг для стали | МПа | 12 |
| — | Время для достижения рабочей прочности | ч | 40-60 |
| — | Время для достижения полной прочности | ч | 72 |
| — | Время для использования готовой смеси | мин | 15 |
| — | Максимально заполняемый зазор | мм | до 2 |
| — | Пропорции | 1 к 1 |