Anti-Friction Coating Molykote 7620

Description

This item’s formula has been modified: N-Methyl-2-pyrrolidone was excluded. New material instead of this one is Molykote D-7409.



Documentation

Material Safety Data Sheet - Molykote 7620 Technical Data Sheet - Molykote 7620

Operating temperatures

-70°C +380°C
  • Applications
  • Advantages
  • Problems to be Solved material
  • The combination of materials
  • Features

Applications

FEATURES

Outstanding lubrication properties
High compressive strength
High temperature resistance
Resistant to oils, greases and solvents
Avoidance of fretting corrosion
High abrasion resistance

APPLICATIONS

For metal/metal combinations with slow to moderately fast movements and moderate to high loads.
Suitable for highly stressed sliding areas with low sliding speeds, oscillating movements or intermittent operations.
For permanent lubrication at high temperatures and also where oils and greases cannot be used.
Used successfully for cylinder head gaskets and exhaust manifold gaskets of combustion engines.

Advantages

  • Cold resistance
  • Termal (heat) resistance
  • Higher load carrying capacity
  • Chemical resistance
  • Working capacity in vacuum
  • Working capacity in moisture
  • Working capacity in dust
  • Radiation resistance
  • Good anticorrosion properties (good corrosion protection)
  • Good adhesion strength
  • Good water washout resistance
  • Good fretting corrosion protection
  • Emergency properties
  • Can be painted over
  • Avoidance of stick-slip

Problems to be Solved material

  • Seizure
  • Stick-slip motion
  • Fretting corrosion
  • Dust sticking onto lubricating surfaces
  • Dust intrusion into lubricating points and abrasive wear
  • Corrosion
  • Lubricant wash-out
  • Lubricant destruction of chemically active medium exposure
  • Lubricant efficiency loss in vacuum
  • Lubricants leaking off or emission due to centrifugal forces
  • Frequent re-lubrication
  • Liquid and consistent lubricants application failure

The combination of materials friction pair

  • Metal - Metal
Стандарт Показатель Ед. изм. Значение
Состояние продуктаСнят с производства, новый продукт - D-7620
ЦветСеро-черный
Антифрикционные добавки (наполнители)Твердые смазочные материалы: дисульфид молибдена - 17%, графит - 1,8%
Прочие составляющиеОрганический связующий агент (полиамид-имид), растворитель
CTM 0242 IСодержание нелетучего остатка%37
Диапазон рабочих температур°Сот -70 до +380
DIN 53 211/5Условная вязкость при 20 °С (тигль DIN5)с105
Температура вспышки°C28
DIN 53 217/2Плотность при 20 °Сг/см31,15
Срок годности при хранениилет2
ASTM D 2625Критическая нагрузка (метод Falex) для поверхности без предварительной обработки / после фосфатирования / после пескоструйной обработкикH-/6,8/-
ASTM D 2714Срок службы (испытание на машине LFW-1 при вращательном движении до коэффициента трения f=0,1 при нагрузке N=2860 H, частоте вращения n=72 об/мин, скорости скольжения v=7,9 м/мин) для поверхности без предварительной обработки / после фосфатирования / после пескоструйной обработкитыс. оборотов-/13/-
ASTM D 2714Срок службы (испытание на машине LFW-1 при возвратно-поступательном движении до коэффициента трения f=0,08 при нагрузке N=900 H, частоте w=89,5 циклов/мин) для поверхности без предварительной обработки / после фосфатирования / после пескоструйной обработкитыс. циклов-/20/-
Условия отверждения (выдержка/температура)мин/°С30/220 (120/150)