Engineering solutions in the field of
lubricants and sealants



Silicone grease formulated to perform in high-temperature applications such as drying and industrial ovens, boilers, steam turbine controls, electric power disconnect switches and power insulator ball-and-socket connections.

Operating temperatures

-18°C +288°C


  • Applications
  • Friction units
  • Advantages
  • Problems to be solved with this material
  • Related videos
  • Recommended by manufacturers
  • The combination of materials
  • Features



Does not melt, even at high temperatures
Superior thermal stability
Superior oxidation resistance
Water resistant


Ideal for use in oven conveyers, kiln dollies, molten salt evacuation pumps, steam turbine regulator links, knife-edge power breakers, etc.

It is used in friction

  • Rolling bearings
  • Sliding bearings
  • Linear bearings
  • Gaskets
  • Electrical contacts


  • Termal (heat) resistance
  • Working capacity in moisture
  • Good anticorrosion properties (good corrosion protection)
  • Good water washout resistance
  • No drop point
  • Compatible with many plastics
  • Compatible with many elastomers

Problems to be solved with this material

  • Corrosion
  • Lubricant wash-out
  • Frequent re-lubrication
  • Plastic and elastomer details deformation and destruction

Related videos

Recommended by manufacturers

  • Quality Bearings & Components

Material combination in friction pair

  • Metal - Metal
Стандарт Показатель Ед. изм. Значение
Базовое маслоСиликоновое
ЗагустительУглеродная сажа
ПрисадкиИнгибитор коррозии
Диапазон рабочих температур°Сот -18 до +288
Фактор скоростимм*об/мин≤ 75000
DIN 51 562Кинематическая вязкость базового масла при 25 °Смм2/c316
ASTM D 217Пенетрация перемешанной смазки (60 циклов)мм/10280
DIN 51 818Класс консистенции по NLGI2
ASTM D 2265Температура каплепадения°C>300
ISO 2811Плотность при 25 °Сг/см31,14
Fed Std 791Выделение масла (24 ч, 150 °C)%4,8
DIN 51 817, Fed Std 791-32/2Выделение масла (168 ч, 40 °C)%2,6
DIN 51 808Стойкость к окислениюкПа40
DIN 51 350 pt.4Нагрузка сваривания (испытание на четырехшариковой машине трения, 1450 об/мин/10 с),Н1500