Grease Molykote
1292
Description
Fluorosilicone grease with polyurea thickener.
Operating temperatures
-40°C +200°C
Pre-packing
100g1kg5kg25kg
- Applications
- Friction units
- Advantages
- Problems to be solved with this material
- Recommended by manufacturers
- The combination of materials
- Features
Applications
FEATURESParticularly suitable for long-term lubrication by virtue of its extremely low tendency towards oxidation
High drop point >250ºC (482ºF); consequently reduced risk of melting and run-out from lubrication point
Wide service temperature range, -40ºC to +200ºC (-40ºF to +392ºF), for short periods, up to 230ºC (446ºF)
High resistance to water and water washout
Resistant to mineral oil, fuels and many chemicals
APPLICATIONS
Lubricating grease for metal/metal combinations with slow to medium-fast movements and medium loads over a wide temperature range.
It is used in friction
Rolling bearings
Sliding bearings
Sliding guideways
Linear bearings
Enclosed gears
Cased flexible shafts
Advantages
- Cold resistance
- Termal (heat) resistance
- High load carrying capacity
- Chemical resistance
- Working capacity in moisture
- Good anticorrosion properties (good corrosion protection)
- Good water washout resistance
- Long service life
- Good shear stability at low temperatures
- Compatible with many plastics
- Compatible with many elastomers
Problems to be solved with this material
- Seizure
- Corrosion
- Lubricant wash-out
- Lubricant destruction of chemically active medium exposure
- Frequent re-lubrication
- Plastic and elastomer details deformation and destruction
Recommended by manufacturers
- Boeing
- Hubbell
- Siemens
- Silea
- Thomson
Material combination in friction pair
- Metal - Metal
- Metal - Plastic
- Metal - Elastomer
- Plastic - Plastic
- Plastic - Elastomer
| Стандарт | Показатель | Ед. изм. | Значение |
|---|---|---|---|
| — | Состояние продукта | Лицензионный продукт | |
| — | Цвет | Беловатый | |
| — | Базовое масло | Фторсиликоновое | |
| — | Загуститель | Полимочевина | |
| — | Диапазон рабочих температур | °С | от -40 до +200 (кратковременно до +230) |
| DIN 51 562 | Кинематическая вязкость базового масла при 25 °С | мм2/c | 1000 |
| DIN ISO 2137 | Пенетрация перемешанной смазки (60 циклов) | мм/10 | 280-340 |
| DIN 51 818 | Класс консистенции по NLGI | 1...2 | |
| DIN ISO 2176 | Температура каплепадения | °C | >250 |
| ISO 2811 | Плотность при 20 °С | г/см3 | 1,28 |
| DIN 51 817 | Выделение масла (стандартный тест) | % | 0,3 |
| DIN 51 350 pt.4 | Нагрузка сваривания (испытание на четырехшариковой машине трения, 1450 об/мин/10 с), | Н | 3400 |
| ASTM D 1478-80 | Момент сопротивления вращению подшипника качения при пониженной температуре -30 °С при запуске / через 20 мин после запуска / в рабочем режиме | H*м | 0,118/0,041/- |
| ASTM D 1478-80 | Момент сопротивления вращению подшипника качения при пониженной температуре -40 °С при запуске / через 20 мин после запуска / в рабочем режиме | H*м | 0,856/0,056/- |