Paste Molykote Cu-7439 Plus

Description

Copper paste for components subjected to high temperatures, high pressures and corrosive influences.



Documentation

Technical Data Sheet - Molykote Cu-7439 Plus Material Safety Data Sheet - Molykote Cu-7439 Plus Material Safety Data Sheet - Molykote Cu-7439 Plus Spray

Operating temperatures

-30°C +650°C

Pre-packing

100g 400ml 500g 1kg 5kg 25kg
  • Applications
  • Friction units
  • Advantages
  • Problems to be Solved material
  • Related videos
  • Recommended by manufacturers
  • The combination of materials
  • Features

Applications

FEATURES

Wide service temperature range
Good pressure resistance
Very adhesive and resistant against water
Good corrosion protection
Low evaporation
No drop point

APPLICATIONS

Well suited for all areas which need to be protected against water, steam and corrosion, e.g. brake mechanisms, flange seals, exhauster bolts.

It is used in friction

  • Rolling bearings
  • Sliding bearings
  • Sliding guideways
  • Threaded connections
  • Spline / key joints
  • Electrical contacts

Advantages

  • Termal (heat) resistance
  • Higher load carrying capacity
  • Working capacity in moisture
  • Working capacity in dust
  • Good anticorrosion properties (good corrosion protection)
  • Good adhesion strength
  • Good water washout resistance
  • No drop point
  • Emergency properties
  • Good wear protection
  • Aerosol
  • Avoidance of stick-slip
  • Provides constant torque for threaded connections
  • Easy mounting / dismounting

Problems to be Solved material

  • Seizure
  • Stick-slip motion
  • Dust intrusion into lubricating points and abrasive wear
  • Corrosion
  • Lubricant wash-out
  • Lubricants leaking off or emission due to centrifugal forces
  • Frequent re-lubrication
  • Difficult mounting / dismounting
  • Lubrication points inaccessibility
  • Unstable torque because of wide range friction coefficient

Related videos

Recommended by manufacturers

  • Nissan
  • Subaru
  • Urbaco
  • Velan

The combination of materials friction pair

  • Metal - Metal
Стандарт Показатель Ед. изм. Значение
ЦветМедный
Базовое маслоЧастично синтетическое
Антифрикционные добавки (наполнители)Медный порошок
ПрисадкиИнгибитор
°СДиапазон рабочих температурот -30 до +300
°СВерхний предел рабочих температур твердых смазочных материалов, входящих в состав продукта+650
DIN 51 562мм2/cКинематическая вязкость базового масла при 40 °С1100
DIN ISO 2137мм/10Пенетрация неперемешанной смазки320-370
DIN ISO 2176°CТемпература каплепаденияНет
DIN 53 217г/см3Плотность при 20 °С1
DIN 51 807 pt.1ст. эмульгированияВодостойкость (3 ч, 90 °C)1
DIN 51 802Степень коррозии по методу Emcor (подшипники качения, дистиллированная вода)0
Н*мНачальный момент отвинчивания (резьба М 12, момент затяжки Ma=80 Н*м, выдержка при 300 °С в течение 21 ч, материал болта № 1.0503 (С 45, 8.8))110
DIN 51 350 pt.4ННагрузка сваривания (испытание на четырехшариковой машине трения, 1450 об/мин/10 с),2500
НКритическая нагрузка (метод Almen-Weiland)>20000
DIN 51 350 pt.5ммПоказатель износа (испытание на четырехшариковой машине трения, 1450 об/мин/800 Н/1 ч)1
Коэффициент трения в болтовом соединении (М12, материал 8.8) для головки болта/для резьбы0,1/0,17
Коэффициент трения для посадки с натягом0,07