Fast curing, self-levelling, elastic 2-component potting compound.

Applications –

• Metal building
• Apparatus- and machine building
• Automotive manufacturing
• Ventilation and climate technique
• Freight car-, vehicle-, container manufacturing
• Plastic manufacturing

Advantages

  • Neutral curing system
  • Excellent adhesion to many substrates without adhesion promoter
  • Resistance against weather influences
  • Resistance against salt water
  • Good resistance against aliphatic solvents
  • Good resistance against watered inorganic asids
  • Good resistance against watered alkalis
  • Good resistance against oils
  • Shock-proofness and vibration-firmness
  • Corrosion protection
  • Non corrosive on surfaces
  • Solvent-free, isocyanate-free, silicone-free
  • Odourless

Good adhesion to materials

  • Aluminium
  • Concrete
  • Wood
  • Stone
  • Ceramics
  • Metals
  • Galvanized and painted surfaces
  • Glass
  • Technical plastics

FEATURES

Стандарт
Показатель
Ед. изм.
Значение
Цвет
Черный
Химический состав
Силаномодифицированный полимер
Внешний вид (консистенция)
Вязко-текучий состав
Диапазон рабочих температур
°С
от -40 до +90 (кратковременно до +120)
Температура нанесения
°С
от +5 до +40
Плотность при 23°С
г/см3
Компонент А 1,39 ±0,05; Компонент Б 1,48 ±0,05
DIN 53 504
Относительное удлинение при разрыве
%
≥300
DIN 53 505
Твердость по Шору А
30
DIN 53 504 S2
Предел прочности на разрыв
МПа
≥1
DIN EN ISO 10563
Усадка во время вулканизации
%
≤4
DIN 53 504 S2
Модуль 100-процентного поперечного растяжения
Н/мм2
≥0,3
Время полимеризации
мин
30