description

Solid lubricating paste for hot forming of metals.

Applications –

FEATURES

High temperature resistance (up to 1150°C)

Reduces friction and wear
Reduces scoring
Increases service life of tools

APPLICATIONS

Suitable for the lubrication of tools for hot forming, particularly on hotflow presses and drop forging, also as a parting agent and slip additive at high temperatures.
Used successfully for the hot bending of flat steel St 37 or St 70, the rolling of the ends of vehicle leafsprings, folding of sheet metal edges, hot rolling of cutters, and drop forging of flywheels made from St 37, as well as for the lubrication of separator plates on chipboard presses.

Advantages

  • Termal (heat) resistance
  • Higher load carrying capacity
  • Good wear protection

Problems to be Solved material

  • Seizure
  • Details sticking after technological operations (pressure forming, molding, etc...)

The combination of materials friction pair

  • Metal - Metal

FEATURES

Стандарт
Показатель
Ед. изм.
Значение
Цвет
Белый
Базовое масло
Минеральное
Загуститель
Загуститель
Антифрикционные добавки (наполнители)
Твердые смазочные материалы
Верхний предел рабочих температур твердых смазочных материалов, входящих в состав продукта
°С
+1150
DIN ISO 2137
Пенетрация неперемешанной смазки
мм/10
250-280
ISO 2811
Плотность при 20 °С
г/см3
1,5
DIN 51 350 pt.4
Нагрузка сваривания (испытание на четырехшариковой машине трения, 1450 об/мин/10 с),
Н
2200
Критическая нагрузка (метод Almen-Weiland)
Н
20000
DIN 51 350 pt.5
Показатель износа (испытание на четырехшариковой машине трения, 1450 об/мин/800 Н/1 ч)
мм
1,0
Сила трения при критической нагрузке (метод Almen-Weiland)
Н
2300