description

High temperature copper thread paste.

Applications –

FEATURES

Can be used over a wide range of temperature(-30°С-22°F to 1100°С/2012°F)
Enables non-destructive dismantling, even after long use at high temperature
High load-carrying capacity
Due stated coefficient of friction, defined pre-stressing forces for bolted joints can be achieved
Good corrosion protection
Good electrical conductivity

APPLICATIONS

For metal/metal combinations that are subjected to high temperatures and frictional contacts which, typically for bolted joints, are free from lead or nickel.
Suitable for lubrication points with low speeds, subjected to high temperatures and corrosive effects, and also require a low and constant coefficient of friction. As a contact lubricant for electrically conducting components.
Used successfully for stud bolts of gas and steam turbines, stud bolts of turbochargers of diesel engines, flanged connections in chemical and petrochemical plants.

It is used in friction

  • Threaded connections
  • Spline / key joints
  • Electrical contacts

Advantages

  • Termal (heat) resistance
  • Very high load carrying capacity
  • Good anticorrosion properties (good corrosion protection)
  • High electrical conductivity
  • No drop point
  • Emergency properties
  • Aerosol
  • Avoidance of stick-slip
  • Provides constant torque for threaded connections
  • Nickel-free
  • Lead-free
  • Easy mounting / dismounting

Problems to be Solved material

  • Seizure
  • Stick-slip motion
  • Corrosion
  • High contact electrical resistance
  • Frequent re-lubrication
  • Difficult mounting / dismounting
  • Lubrication points inaccessibility
  • Unstable torque because of wide range friction coefficient

Recommended by manufacturers

  • Demag Plastics Machinery GmbH
  • Dreizler
  • Halfen
  • IMA

The combination of materials friction pair

  • Metal - Metal

FEATURES

Стандарт
Показатель
Ед. изм.
Значение
Цвет
Медный
Базовое масло
Минеральное
Загуститель
Загустители
Антифрикционные добавки (наполнители)
Дисульфид молибдена, медный порошок и другие твердые смазочные материалы
Верхний предел рабочих температур твердых смазочных материалов, входящих в состав продукта
°С
+1100
DIN ISO 2137
Пенетрация неперемешанной смазки
мм/10
250-280
DIN ISO 2176
Температура каплепадения
°C
Нет
ISO 2811
Плотность при 20 °С
г/см3
1,4
Начальный момент отвинчивания (резьба М 12, момент затяжки Ma=56 Н*м, выдержка при 540 °С в течение 21 ч, материал болта № 1.7709 (21CrMoNiV57))
Н*м
120
DIN 51 350 pt.4
Нагрузка сваривания (испытание на четырехшариковой машине трения, 1450 об/мин/10 с),
Н
4800
Критическая нагрузка (метод Almen-Weiland)
Н
20000
DIN 51 350 pt.5
Показатель износа (испытание на четырехшариковой машине трения, 1450 об/мин/400 Н/1 ч)
мм
0,6
DIN 51 350 pt.5
Показатель износа (испытание на четырехшариковой машине трения, 1450 об/мин/800 Н/1 ч)
мм
1,1
Сила трения при критической нагрузке (метод Almen-Weiland)
Н
1700
Коэффициент трения в болтовом соединении (М12, материал 8.8) для головки болта/для резьбы
0,09/0,14