Grease Molykote
X5-6020
Description
Mineral oil grease especially for plastics.
Operating temperatures
-30°C +150°C
Pre-packing
1kg5kg25kg
- Applications
- Friction units
- Advantages
- Problems to be solved with this material
- Recommended by manufacturers
- The combination of materials
- Features
Applications
FEATURESCompatible with most plastics
Can be used for plastic-plastic contact, metal-metal contact and plastic-metal contact
White color does noi damage appearance of equipment
Does not contain silicone thereby preventing problems with contact point failures
APPLICATIONS
Automobiles, electrical appliances, precision equipment, audio equipment, and office equipment that have plastic parts.
It is used in friction
Sliding bearings
Enclosed gears
Advantages
- Termal (heat) resistance
- High load carrying capacity
- Working capacity in moisture
- Working capacity in dust
- Good anticorrosion properties (good corrosion protection)
- Good wear protection
- Compatible with many plastics
- Compatible with many elastomers
- Avoidance of stick-slip
Problems to be solved with this material
- Seizure
- Stick-slip motion
- Dust intrusion into lubricating points and abrasive wear
- Corrosion
- Frequent re-lubrication
- Plastic and elastomer details deformation and destruction
Recommended by manufacturers
- Toshiba
Material combination in friction pair
- Metal - Metal
- Metal - Plastic
- Plastic - Plastic
| Стандарт | Показатель | Ед. изм. | Значение |
|---|---|---|---|
| — | Цвет | Белый | |
| — | Базовое масло | Минеральное | |
| — | Загуститель | Литиевое мыло | |
| — | Антифрикционные добавки (наполнители) | Твердые смазочные материалы | |
| — | Диапазон рабочих температур | °С | от -30 до +150 |
| — | Кинематическая вязкость базового масла при 40 °С | мм2/c | 80 |
| JIS K 2220 | Пенетрация перемешанной смазки (60 циклов) | мм/10 | 315 |
| DIN 51 818 | Класс консистенции по NLGI | 1...2 | |
| JIS K 2220 | Температура каплепадения | °C | 190 |
| — | Плотность при 20 °С | г/см3 | 0,96 |
| JIS K 2220 | Потери на испарение (22 ч, 100 °C) | % | 0,7 |
| JIS K 2220 | Выделение масла (24 ч, 100 °C) | % | 4 |
| JIS K 2220 | Степень коррозии на медной пластине | 1a | |
| ASTM D 2266 | Показатель износа (испытание на четырехшариковой машине трения, 1200 об/мин/392 Н/75 °C/1 ч) | мм | 0,5 |
| — | Совместимость с пластиками (тест на пенополистироле при 60 °С в течение 24 ч) | Нет изменений |