description

It is a new modified version of Molykote D-10 Coating: N-Methyl-2-Pyrrolidone solvent (N-МP) in it is replaced with gamma-butyrolactone.

Applications –

FEATURES

Excellent resistance to oil, grease, gasoline, diesel and solvents
Long-term wear protection
Highly viscous and suitable for screen-printing
High temperature resistance

APPLICATIONS

For metal/metal combinations involving slow to medium speeds and low to medium loads.
Suitable for the permanent lubrication of heavily loaded friction contacts involving low to high speeds, in direct contact with motor oils, gasoline, diesel or grease.
Used in automotive applications like pistons of internal gasoline and diesel combustion engines, compressors and piston pumps, pneumatic and hydraulic systems; and other applications that require help to reduce piston and cylinder wall wear during break-in, cold-start and ongoing operation situations.

It is used in friction

  • Sliding bearings
  • Sliding guideways
  • Enclosed gears
  • Piston-cylinder-group (unit)
  • Electrical contacts

Advantages

  • Cold resistance
  • Termal (heat) resistance
  • Chemical resistance
  • Working capacity in moisture
  • Working capacity in dust
  • Good adhesion strength
  • Good water washout resistance
  • Long service life
  • Emergency properties
  • Avoidance of stick-slip

Problems to be Solved material

  • Seizure
  • Stick-slip motion
  • Dust sticking onto lubricating surfaces
  • Dust intrusion into lubricating points and abrasive wear
  • Lubricant wash-out
  • Lubricant destruction of chemically active medium exposure
  • Lubricants leaking off or emission due to centrifugal forces
  • Frequent re-lubrication
  • Liquid and consistent lubricants application failure

The combination of materials friction pair

  • Metal - Metal

FEATURES

Стандарт
Показатель
Ед. изм.
Значение
Цвет
Серо-черный
Антифрикционные добавки (наполнители)
Твердые смазочные материалы: графит - 15%
Прочие составляющие
Органический связующий агент (полиамид-имид), растворитель
Диапазон рабочих температур
°С
от -40 до +340
ASTM D 1084 Method B
Динамическая вязкость при 20 °С
Па*с
35
ASTM D 56
Температура вспышки
°C
77
ASTM D 1475
Плотность при 20 °С
г/см3
1,3
Срок годности при хранении
лет
1
ASTM D 2625
Критическая нагрузка (метод Falex) для поверхности без предварительной обработки / после фосфатирования / после пескоструйной обработки
кH
-/5,5/-
DIN 51 834
Срок службы (испытание на машине SRV при трении сферы по диску при нагрузке N=15 H, контактном давлении P=1160 МПа, скорости V=40 мм/с, температуре T=50 °С, относительной влажности H=40 %) для поверхности после фосфатирования
ч
>12
Коэффициент трения (испытание при нагрузке N=50 H, контактном давлении P=150 МПа, скорости V=120 мм/с, температуре T=50 °С, относительной влажности H=40 % и добавлении трех капель моторного масла)
0,12
Условия отверждения (выдержка/температура)
мин/°С
20/200