description

Extremely pure, solid lubricant paste for bolted joints. It contains no lead, nickel, sulphur, chlorine or fluorine.

Applications –

FEATURES

Compatible with high temperatures (1400°C)
Excellent load-carrying capacity and seize protection
Sulphur content of less than 250ppm, with a total halogen content (including chlorine) of less that 20Oppm
Low seepage, so it can be used in places wherein cleanliness is required
Allows screws to be removed easily even after extended periods of use at high temperatures
Does not include components that become brittle at high temperatures

APPLICATIONS

Prevents seize of screws used at high temperatures.
Aprroved for use by many manufacturers of set screws used in power plant turbines, and manufacturers of steam valve joints

It is used in friction

  • Sliding bearings
  • Sliding guideways
  • Threaded connections
  • Spline / key joints

Advantages

  • Cold resistance
  • Termal (heat) resistance
  • Very high load carrying capacity
  • Good adhesion strength
  • Emergency properties
  • Avoidance of stick-slip
  • Provides constant torque for threaded connections
  • Nickel-free
  • Lead-free
  • Easy mounting / dismounting

Problems to be Solved material

  • Seizure
  • Stick-slip motion
  • Lubricants leaking off or emission due to centrifugal forces
  • Frequent re-lubrication
  • Difficult mounting / dismounting
  • Unstable torque because of wide range friction coefficient

Recommended by manufacturers

  • Allweiler
  • Biral
  • Endress+Hauser
  • Flowserve
  • General Electric
  • Naval sea systems command
  • Pratt & Whitney
  • Siemens
  • Velan
  • WILO

The combination of materials friction pair

  • Metal - Metal

FEATURES

Стандарт
Показатель
Ед. изм.
Значение
Цвет
Серо-черный
Базовое масло
Минеральное
Антифрикционные добавки (наполнители)
Твердые смазочные материалы
Содержание галогенов
%
<0,02
Содержание серы
%
<0,025
Верхний предел рабочих температур твердых смазочных материалов, входящих в состав продукта
°С
+1400
JIS K 2220
Пенетрация перемешанной смазки (60 циклов)
мм/10
310-340
Класс консистенции по NLGI
1
Плотность при 20 °С
г/см3
1,21
ASTM D 2596
Нагрузка сваривания (испытание на четырехшариковой машине трения, 1500 об/мин/60 с)
Н
4000
ASTM D 2266
Показатель износа (испытание на четырехшариковой машине трения, 1200 об/мин/392 Н/75 °C/1 ч)
мм
0,75
Коэффициент трения в болтовом соединении (М12, материал 8.8) для головки болта/для резьбы
0,09/0,15