description

Silicone based MoS2 paste.

Applications –

FEATURES

Paste lubrication up to +230°C (+446°F), dry lubrication up to +450°C (+842°F)
Good water resistance
Good volatilization properties
Compatible with many types of elastomers and plastics (test for compatibility)

APPLICATIONS

Suitable for lubrication points with low to moderate loads and low speeds which are subjected to water and extreme temperatures. At temperatures above 230°C (446°F), the carrier volatilizes leaving virtually no residue, and the remaining dry sliding film itself takes over the lubrication up to +450°C (+842°F)
Suitable for lubricating parts consisting of materials that are not resistant to mineral oils
This product is used successiully on metal/metal combinations with frictional and contact surfaces, brake anchor plates and the brake pistons of disc brakes.

It is used in friction

  • Sliding bearings
  • Interference fits
  • Strips
  • Spline / key joints

Advantages

  • Cold resistance
  • Termal (heat) resistance
  • Working capacity in moisture
  • Emergency properties
  • Compatible with many plastics
  • Compatible with many elastomers
  • Avoidance of stick-slip

Problems to be Solved material

  • Seizure
  • Stick-slip motion
  • Frequent re-lubrication
  • Plastic and elastomer details deformation and destruction

Recommended by manufacturers

  • Acura
  • Emerson Process Management
  • Honda
  • Infiniti
  • Naval sea systems command
  • Nissan
  • Rover Company
  • Subaru

The combination of materials friction pair

  • Metal - Metal

FEATURES

Стандарт
Показатель
Ед. изм.
Значение
Цвет
Серо-черный
Базовое масло
Силиконовое
Загуститель
Литиевое мыло
Антифрикционные добавки (наполнители)
Дисульфид молибдена
Диапазон рабочих температур
°С
от -45 до +230
Верхний предел рабочих температур твердых смазочных материалов, входящих в состав продукта
°С
+350
DIN 51 562
Кинематическая вязкость базового масла при 25 °С
мм2/c
125
DIN ISO 2137
Пенетрация неперемешанной смазки
мм/10
280-330
ISO 2811
Плотность при 20 °С
г/см3
1,95
DIN 51 350 pt.4
Нагрузка сваривания (испытание на четырехшариковой машине трения, 1450 об/мин/10 с),
Н
2000