description

1-component elastic adhesive with an especially high tensile strength which is designed for bonding large component with dissimilar thermal expansion coefficients.

Applications –

• Metal construction
• Apparatus- and machine building
• Automotive manufacturing
• Ventilation and air-conditioning equipment
• Freight car-, vehicles and container manufacturing
• Polymer manufacturing

Advantages

  • Neutral curing system
  • Excellent adhesion to many substrates without adhesion promoter
  • Resistance against weather influences
  • Resistance against salt water
  • Good resistance against aliphatic solvents
  • Good resistance against watered inorganic asids
  • Good resistance against watered alkalis
  • Good resistance against oils
  • Paintability by powder staining
  • Paintability (also wet on wet)
  • Shock-proofness and vibration-firmness
  • Solvent-free, isocyanate-free, silicone-free
  • Odourless

Good adhesion to materials

  • Aluminium
  • Concrete
  • Wood
  • Stone
  • Ceramics
  • Metals
  • Plexiglas
  • Galvanized and painted surfaces
  • Glass
  • Technical plastics

FEATURES

Стандарт
Показатель
Ед. изм.
Значение
Цвет
Белый, серый, черный
Химический состав
Силаномодифицированный полимер
Внешний вид (консистенция)
Нестекающая паста
Диапазон рабочих температур
°С
от -40 до +90
Температура нанесения
°С
от +5 до +40
Плотность при 23°С
г/см3
1,68 ±0,05
Время до образования первичной пленки
мин
8
DIN 53 504
Относительное удлинение при разрыве
%
≥500
DIN 53 505
Твердость по Шору А
56
DIN 53 504 S2
Предел прочности на разрыв
МПа
~5
DIN EN ISO 10563
Усадка во время вулканизации
%
≤13
Отверждение вглубь от поверхности через 24/48 ч.
мм
≥3,5 / ≥4,5
DIN 53 504 S2
Модуль 100-процентного поперечного растяжения
Н/мм2
≥1,5